Pulp beating (refining) freeness tester TP-C10 is used to measure the rate of dilution of pulp suspended water materials and to determine de-watering time. It is adopted with spring pre-tightening mechanism keeps the rubber sealing ring of the sealing hammer body in contact with the bottom of the water filtering tube. This increases the sealing performance of the sealing hammer body.
Buy Now View Catalog| Measurement range | 0 to 100° SR |
| Slider weight | |
| Slider size | |
| Testing accuracy | |
| Dimension of working plate | |
| Speed of slider | |
| Slider stroke | |
| Specimen size | |
| Division value | |
| Number of specimen holders | |
| Metal Cylinder inner area | |
| Metal Cylinder height | |
| Metal roller width | |
| Metal roller weight | |
| Absorbency paper | |
| Absorbency speed | |
| Sealed testing speed | 100 ± 10 mm/s |
| Volume of distilled water | 1000 ± 5 ml |
| Sample diameter | |
| Sample error | |
| Sample Thickness | |
| Draining time | 149 ± 1 s |
| Residual water volume | 7.85 to 8 ml |
| Hydraulic pressure | >0.3 MPa |
| Dimension | 450×250×1100 mm |
| Net Weight | 40 kg |
Pulp beating freeness tester has applications in pulp & paper industry, packaging industry.
Sample size (L*B) : 230×50 mm (can join short samples together)
Rub pressure : 20 ± 0.2 N
Friction speed : 43 times / min
Sample (size) length : Diameter ≥30 mm, Thickness ≤ 40 mm
Measurement mode : Diffuse reflection factor Rx, Ry, Rz, stimulus value Y10, X10, Z10, chromaticity coordinates x10, y10, z10; lightness L *, chroma a * b *, chroma C * ab, hue angle h * ab, dominant wavelength λd, excitement purity Pe, color difference ΔE * ab, lightness difference ΔL *, chroma difference ΔC * ab, hue difference ΔH * ab, Hunter system L , A, b
Stability : ≤ 0.1 within 30 min
Measuring range : 0 to 20 mm
Accuracy : 0.01 mm
Gauge : Analogue gauge display
Sample diameter : 125 mm
Sample error : ± 0.2 mm
Sample Thickness : 0.1 to 1.0 mm
Measuring range : 0 to 1000 ml/min
Test area : 10 ± 0.02 cm2
Area differential pressure : 1 ± 0.01 kPa
Sample (size) length : Diameter ≥30 mm, Thickness ≤ 40 mm
System : D/0 lighting geometrical viewing conditions, diffuser diameter (d) 150mm, testing hole diameter 30mm
Light source : D65 as illuminating source
Measuring scope : ( 1 to 9999) s, divided in to (1 to 15) s, (15 to 300) s, (300 to 9999) s, the automatic (no. more than 200 s)
Accuracy : ±0.1 s within 300 s
Vacuum system volume (ml) : Bigger volume: 380 ± 1
Smaller volume: 38 ± 1
Measuring range : 0 to 4 mm
Accuracy : 0.01 or 0.001 mm
Gauge : Analogue gauge display
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Total test force dwell time | 0 to 30 S |
| Preliminary test force | 98 N |
| Total test force | 588, 980, 1471 N |
| Total test force dwell time | 1 to 30 S |
| Test angle | 60° |
| Gloss aperture | 2 × 3 mm |
| Measurement range | 0 to 1000 GU |
| Vacuum degree | 0 to 90 KPa |
| Accuracy | 1 % FS |
| Resolution | 0.1 KPa |
| The maximum temperature | 300°C |
| Temperature fluctuation | Within ± 0.5°C |
| Temperature uniformity | Within ± 1°C |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Measuring range | 0.001 to 9999 |
| Stability | A (absorbency of light) <0.003 within 3 mins |
| Linearity error | <3.0 % |
| Mixed capacity | 0.5 to 1 kg, 2 to 3 kg, 5 to 7 kg |
| Temperature range | RT to 300°C |
| Temperature control system | PID control |
| Temperature control range | Room temperature to -70 ℃ (room temperature ≤ 25 ℃） |
| Temperature accuracy | ± 0.3 ℃ |
| Impact speed | 0℃ to -30℃ around 2.5 ℃/min -30℃ to -40℃ around 2.5 ℃/min -40℃ to -70℃ around 2.0 ℃/min |